濟南鋁板http://www.7075lu.com/廢棄品處理時首要是要對廢鋁品進行初級分類、分級堆積，如純鋁、變形鋁合金、鍛造鋁合金、混合料等。關(guān)于廢鋁制品，須進行拆解，去掉與鋁料銜接的鋼鐵及其他有色金屬件，再經(jīng)清潔、破碎、磁選、烘干等工序制成廢鋁料。關(guān)于輕薄松懈的片狀廢舊鋁件，如汽車上的鎖緊臂、速度齒輪軸套以及鋁屑等，要用液壓金屬打包機鎮(zhèn)壓成包。關(guān)于鋼芯鋁絞線，應(yīng)先別離鋼芯，然后將鋁線繞成卷。
Jinan aluminum waste disposal for scrap when the primary is to conduct primary product sorting, grading accumulation, such as aluminum, wrought aluminum alloy, forged alloy, mixed materials. About scrap products required for dismantling, removing material with aluminum, steel and other non-ferrous metals convergence pieces, and then the cleaning, crushing, magnetic separation, drying and other processes made of scrap material. Lax on thin sheet of scrap aluminum, such as locking arm on the car, the speed of the gear sleeve and aluminum shavings, etc., use of hydraulic metal baler repression into packets. About ACSR, you should leave the steel core and aluminum wire wound into a roll.

濟南鋁板http://www.7075lu.com/廢棄品中常富含油漆、油類、塑料、橡膠等有機非金屬雜質(zhì)。在回爐鍛煉前，必須設(shè)法加以鏟除。關(guān)于導(dǎo)線類廢鋁，通?？蛇x用機械研磨或剪切剝離、加熱剝離、化學(xué)剝離等辦法去掉包皮。當(dāng)前國內(nèi)不少公司用高溫?zé)g的辦法去掉絕緣體，燒蝕進程中會產(chǎn)生很多的有害氣體，嚴(yán)重地污染空氣。
Jinan waste products often rich in aluminum paint, oil, plastics, rubber and other organic non-metallic impurities. Before refresher training, must seek to eradicate. About wire scrap class, usually the choice of mechanical grinding or shear peel, peel heating, chemical peel and other methods to remove the foreskin. Many domestic companies to get rid of the current high-temperature ablation approach insulator ablation process will produce a lot of harmful gases, serious air pollution.　　

濟南鋁板廢棄品處理時要進行廢鋁的液化別離，將廢鋁雜料的預(yù)處理與從頭熔鑄相結(jié)合，既縮短了工藝流程，又能夠最大極限地防止空氣污染，并且使得凈金屬 的收回率大大提高。廢鋁液化別離設(shè)備中有一個答應(yīng)氣體微粒經(jīng)過的過濾器，在液化層，鋁沉淀于底部，廢鋁中附著的油漆等有機物在450℃以上分解成氣體、焦油和固體炭，再經(jīng)過別離器內(nèi)部的氧化設(shè)備徹底燃燒。廢料經(jīng)過旋轉(zhuǎn)鼓拌和，與倉中的溶解液混合，砂石等雜質(zhì)別離到砂石別離區(qū)，被廢料帶出的溶解液經(jīng)過收回螺旋槳回來液化倉。
Jinan aluminum processing waste products to be liquefied parting scrap will scrap pretreatment and miscellaneous material cast from scratch by combining both shorten the process, but also to the maximum limit to prevent air pollution,

and makes the metal recovery rate of net greatly increased. Scrap liquefaction parting device has a promised gas particles through the filter, the liquefied layer of aluminum deposited on the bottom, aluminum paint and other organic

matter in the attached above 450 ℃ decomposed into gas, tar and solid carbon, and then after parting device internal oxidation apparatus complete combustion. After rotating drum mixing the waste with the positions of the lysate mix,

sand and other impurities leave to leave the gravel area, dissolving liquid wastes are brought out through the back of the propeller back liquefaction warehouse.