1、濟南鋁板http://www.7075lu.com/化學拋光光亮度沒有達到預期的目標，其原因可從特殊鋁材的生產工藝和化學拋光工藝這兩方面分析。建議采用鋁純度99.70%及其以上級別的鋁錠來生產特殊鋁材；鋁材加工工藝中質量控制為化學拋光得到高光亮度表面奠定基礎。
Jinan aluminum chemical polishing brightness does not achieve the desired objectives, the reason can be analyzed from a special aluminum production process and chemical polishing process in these two areas. Recommended and above 99.70% purity aluminum ingots for the production of special grade aluminum; aluminum processing quality control for the chemical polishing process to obtain a high surface brightness foundation.

2、濟南鋁板化學拋光時間不足，溫度不夠，攪拌不充分，槽液老化等也會使化學拋光表面光亮度不足。槽液的相對密度較大，防止鋁材浮出拋光槽液的液面，致使上部鋁材光亮度不足。水的影響造成光亮度不足，往往容易被忽視。最好用干燥的鋁材進入化學拋光槽液，杜絕水分的帶入。
Jinan aluminum chemical polishing enough time temperature is not enough to sufficiently stir, bath aging, also causes less chemical polishing surface brightness. The relative density of the bath is large, preventing polished aluminum floating bath liquid, resulting in lack of upper aluminum brightness. The effect of water shortage caused by the brightness, often easily overlooked. Best to use dry chemical polishing of aluminum into the bath, to prevent moisture into.

3、濟南鋁板http://www.7075lu.com/化學拋光后的鋁材表面上附著有一層白色的沉積物，且分布不均勻，附著物底部的鋁材表面有可能被腐蝕。通常，該缺陷是因為化學拋光槽液中溶鋁量太高所致，需采取措施調整槽液中的溶鋁量到正常的范圍內。
Jinan aluminum chemically adhered on the aluminum surface after polishing layer of white sediment, and uneven distribution, the bottom of the aluminum surface attachments may be corroded.Typically, this defect is due to a chemical polishing bath soluble aluminum content is too high due to the need to take measures to adjust the amount of aluminum melting bath to within normal range.